201 Stainless Steel Pipe
7
Nov-01/2024
201 Stainless Steel Pipe DescriptionType 201 stainless steel is an austenitic chromium-nickel-manganese stainless steel, which is developed to save nickel. Type 201 is a low-cost alternative to traditional Cr-Ni stainless steels such as 301 and 304. The nickel is replaced by added manganese and nitr
- Categories:Stainless Steel Pipe
- tages:
201 Stainless Steel Pipe Description
Type 201 stainless steel is an austenitic chromium-nickel-manganese stainless steel, which is developed to save nickel. Type 201 is a low-cost alternative to traditional Cr-Ni stainless steels such as 301 and 304. The nickel is replaced by added manganese and nitrogen. It cannot be hardened by heat treatment, but can reach high tensile strength by cold working. Type 201 is essentially non-magnetic in the annealed condition and becomes magnetic upon cold working. In many applications, the 201 type may replace the 301 type.
Product Parameters
Product Name 201 Stainless Steel Pipe Type Steel Pipe Outer diameter Round Tube 4mm-200mm Square Tube 10*10mm-100*100mm Rectangular Tube 10*20mm-50*100mm Wall Thickness 0.6mm-6.0mm Length 1-6 meters, Length can be customized Standard ASTM, AISI, JIS, GB, DIN, EN, etc. Surface Black, Bright Polished, Rough Turning, Matt Surface Treatment, No. 4. BA, etc. Scope of Application Common applications for stainless steel pipes include food processing, Textile operations, Breweries, Water treatment plants, Oil and gas processing, Fertilizers and pesticides, Chemical applications, Construction, Pharmaceuticals, Auto parts, etc. Certificate ISO, SGS, BV, etc. Production Technology Hot Rolling, Cold Rolling Edge Processing Edging, Trimming
Chemical Composition
C Si Mn Cr Ni S P ≤ 0.15 ≤ 0.75 5.50~7.50 16.00~18.00 3.50~5.50 ≤ 0.03 ≤ 0.06
Mechanical Properties
Tensile Strength Kb (MPa) Yield Strength σ0.2 (MPa) Elongation D5 (%) Hardness ≥ 520 ≥ 275 ≥55-60 ≤183HB；≤ 100 HRB
Physical Performance
Density(g/cm³) Modulus of Elasticity(Gpa) Coefficient of Thermal Expansion(10-6/°C) Coefficient of Thermal Conductivity(W/m*K) Resistivity(μohm.in) 7.8 197 15.7 16.2 27
-