201 Stainless Steel Plate
7
Oct-31/2024
201 Stainless Steel Plate DescriptionType 201 stainless steel is an austenitic chromium-nickel-manganese stainless steel, which is developed to save nickel. Type 201 is a low-cost alternative to traditional Cr-Ni stainless steels such as 301 and 304. The nickel is replaced by added manganese and nit
- Categories:Stainless Steel Plate
- tages:
201 Stainless Steel Plate Description
Type 201 stainless steel is an austenitic chromium-nickel-manganese stainless steel, which is developed to save nickel. Type 201 is a low-cost alternative to traditional Cr-Ni stainless steels such as 301 and 304. The nickel is replaced by added manganese and nitrogen. It cannot be hardened by heat treatment, but can reach high tensile strength by cold working. Type 201 is essentially non-magnetic in the annealed condition and becomes magnetic upon cold working. In many applications, the 201 type may replace the 301 type.
Product Parameters
Product Name 201 Stainless Steel Plate Type Plate Thickness 0.3mm-200mm Length 2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc. Width 40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc. Standard ASTM, AISI, JIS, GB, DIN, EN, etc. Surface BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. Scope of Application Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. Certificate ISO, SGS, BV, etc. Production Technology Hot Rolling, Cold Rolling Edge Processing Edging, Trimming
Chemical Composition
C Si Mn Cr Ni S P ≤ 0.15 ≤ 0.75 5.50~7.50 16.00~18.00 3.50~5.50 ≤ 0.03 ≤ 0.06
Mechanical Properties
Tensile Strength Kb (MPa) Yield Strength σ0.2 (MPa) Elongation D5 (%) Hardness ≥ 520 ≥ 275 ≥55-60 ≤183HB；≤ 100 HRB
Physical Performance
Density(g/cm³) Modulus of Elasticity(Gpa) Coefficient of Thermal Expansion(10-6/°C) Coefficient of Thermal Conductivity(W/m*K) Resistivity(μohm.in) 7.8 197 15.7 16.2 27