201 Stainless Steel Bar
13
Nov-01/2024
201 Stainless Steel Bar DescriptionType 201 stainless steel is an austenitic chromium-nickel-manganese stainless steel, which is developed to save nickel. Type 201 is a low-cost alternative to traditional Cr-Ni stainless steels such as 301 and 304. The nickel is replaced by added manganese and nitro
- Categories:Stainless Steel Bar
- tages:
201 Stainless Steel Bar Description
Type 201 stainless steel is an austenitic chromium-nickel-manganese stainless steel, which is developed to save nickel. Type 201 is a low-cost alternative to traditional Cr-Ni stainless steels such as 301 and 304. The nickel is replaced by added manganese and nitrogen. It cannot be hardened by heat treatment, but can reach high tensile strength by cold working. Type 201 is essentially non-magnetic in the annealed condition and becomes magnetic upon cold working. In many applications, the 201 type may replace the 301 type.
Product Parameters
Product Name 201 Stainless Steel Bar Type Steel Bar Outer Diameter Round Bar 4mm-500mm Hexagon Bar 18mm-57mm (11/16″ to 2-3/4″) Square Bar 18mm-47mm (11/16″ to 1-3/4″) Flat Steel 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized Length 1-6 meters, Length can be customized Standard ASTM, AISI, JIS, GB, DIN, EN, etc. Surface Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. Scope of Application Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc.
Chemical Composition
C Si Mn Cr Ni S P ≤ 0.15 ≤ 0.75 5.50~7.50 16.00~18.00 3.50~5.50 ≤ 0.03 ≤ 0.06
Mechanical Properties
Tensile Strength Kb (MPa) Yield Strength σ0.2 (MPa) Elongation D5 (%) Hardness ≥ 520 ≥ 275 ≥55-60 ≤ 183HB；≤ 100 HRB
Physical Performance
Density(g/cm³) Modulus of Elasticity(Gpa) Coefficient of Thermal Expansion(10-6/°C) Coefficient of Thermal Conductivity(W/m*K) Resistivity(μohm.in) 7.8 197 15.7 16.2 27
-