316 Stainless Steel Bar
22
Nov-01/2024
316 Stainless Steel Bar DescriptionGrade 316 stainless steel is an austenitic form of stainless steel with a molybdenum content of 2-3%. The addition of molybdenum makes the metal more resistant to pitting and corrosion and improves its resistance to exposure to high temperatures. This grade of stai
- Categories:Stainless Steel Bar
- tages:
316 Stainless Steel Bar Description
Grade 316 stainless steel is an austenitic form of stainless steel with a molybdenum content of 2-3%. The addition of molybdenum makes the metal more resistant to pitting and corrosion and improves its resistance to exposure to high temperatures. This grade of stainless steel is particularly effective when used in acidic environments. With this metal, corrosion caused by acetic acid, hydrochloric acid and other forms of acid can be prevented.
Product Parameters
Product Name 316 Stainless Steel Bar Type Steel Bar Outer Diameter Round Bar 4mm-500mm Hexagon Bar 18mm-57mm (11/16″ to 2-3/4″) Square Bar 18mm-47mm (11/16″ to 1-3/4″) Flat Steel 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized Length 1-6 meters, Length can be customized Standard ASTM, AISI, JIS, GB, DIN, EN, etc. Surface Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. Scope of Application Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc.
Chemical Composition
C Si Mn Cr Ni S P Mo ≤ 0.03 ≤ 0.75 ≤ 2.0 16.0～18.0 10.0～14.0 ≤ 0.03 ≤ 0.045 2.0～3.0
Mechanical Properties
Tensile Strength Kb (MPa) Yield Strength σ0.2 (MPa) Elongation D5 (%) Hardness ≥480 ≥177 ≥ 40 ≤ 187HB;≤ 90HRB;≤ 200HV
Physical Performance
Density(g/cm³) Modulus of Elasticity(Gpa) Coefficient of Thermal Expansion(10-6/°C) Coefficient of Thermal Conductivity(W/m*K) Resistivity(ΜΩ. cm) 7.99 193 16.0 16.2 74
-