Inconel 601 Bar
5
Nov-04/2024
Inconel 601 Bar DescriptionInconel 601 is a nickel-based high-temperature alloy mainly composed ofnickel, chromium, aluminum and iron. Among them, nickel accounts for the majority, with a content generally above 58%, while chromium and aluminum account for about 19% and 1.0%
- Categories:Alloy Bar
- tages:
Inconel 601 Bar Description
Inconel 601 is a nickel-based high-temperature alloy mainly composed of nickel, chromium, aluminum and iron. Among them, nickel accounts for the majority, with a content generally above 58%, while chromium and aluminum account for about 19% and 1.0% respectively. In addition, it also contains small amounts of elements such as copper and manganese, which can enhance the strength and corrosion resistance of the material. Inconel 601 bar has excellent high temperature strength, corrosion resistance and oxidation resistance. At high temperatures, its strength and hardness can be maintained at a high level, while having good plasticity and toughness. In an acidic environment, Inconel 601 bar shows good corrosion resistance and can effectively resist erosion by corrosive media such as chloride ions and sulfides.
Product Parameters
Product Name | Inconel 601 Bar | |
Outer Diameter | Round Bar | 4mm-500mm |
Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
Length | 1-6 meters, Length can be customized | |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
Surface | Black, Bright Polished, Rough Turning, Matt Surface Treatment, NO.4, BA, etc. | |
Certificate | ISO, SGS, BV | |
Production Technology | Hot Rolling, Cold Rolling | |
Chemical Composition
C | Al | Si | S | Cr | Mn | Fe | Ni | Cu |
0.1 max | 1.0-1.7 | 0.5 max | 0.015 max | 21.0-25.0 | 1.0 max | Remainder | 58.0-63.0 | 1.0 max |
Mechanical Properties
Tensile Strength (ksi) | 0.2% Yield Strength (ksi) | Elongation% in 2 inches |
80 | 30 | 30 |
Physical Performance
Units | Temperature in°C | |
Density | 8.11 g/cm³ | Room |
Specific Heat | 0.107 Kcal/kg.C | 20° |
Melting Range | 1360-1411°C | - |
Modulus of Elasticity | 206.5 KN/mm² | 20° |
Electrical Resistivity | 118 µΩ.cm | 20° |
Coefficient of Expansion | 13.75 µm/m °C | 20 - 100° |
Thermal Conductivity | 11.2 w/m-° K | 20° |
Scope of Application
The 601 characteristics of Inconel make it widely used in the fields of heat treatment, chemical treatment, pollution control, aerospace and power generation. Therefore, it is not recommended to use the alloy 601 in a strongly reduced sulfur-containing environment.
-